COPPER PHOSPHORUS BRAZING ALLOYS

COPPER PHOSPHORUS BRAZING ALLOYS

Country of Origin:
Taiwan

Detail Specifications / Descriptions

Description :



The compound with high proportion of phosphorus will result in a more active and fluid alloy which can flow over a larger area. The alloy usually has a
smaller melting range and best used on filler joint. Higher proportion of silver alloy will result in a fluid which is easier to be controlled by operators.
The silver alloy with less phosphorus may have a melting range which suitable for filling gaps. Generally, higher silver content alloy can bear hotter or
longer heating cycle. Moreover, the resulted joints have better ductility.
MAIN USE : Refrigerator, air conditioner, heating exchanger , electric machine, brass alloy and others.




Silver Brazing Alloys

Chemical Composition

AWS/JIS


Reference Data


Density
kg/cm3



Application




Ag


Cu


P


Other elements


Spec Class


Solidus oC


Liquidus oC




Cl-P007


-


93


7


<0.2


BCuP-2


705


805


8.05


0% of silver, the alloy fluid can flow along the joint border which can reduce the alloy spread the surface.




Cl-P008


-


92


8


<0.2





700


800


8.0


0% of silver, rapid and extensive fluidity. The fluid may spread the surface which is not easy to be controlled by operator




Cl-001


1


92


7


<0.2





640


800


8.1


Instead of CI-002 for saving cost




Cl-002


2


91


7


<0.2


BCuP-6


645


740


8.1


2% of silver spread extensively; Best used on filler joint.




Cl-003


3


91


6


<0.2





630


785


8.2


Instead of CI-005 for saving cost




Cl-005


5


89


6


<0.2


BCuP-3


640


805


8.2


5% of silver, used as a temperature inhibitor.




Cl-006


6


86.8


7.2


<0.2


BCuP-4


645


725


8.2


Good fluidity & similar to CI-005.




Cl-101


10


84.5


5.5


<0.2














Less silver content than Cl-151, economical product.




Cl-151


15


80


5


<0.2


BCuP-5


645


770


8.4


Lower melting range. Can be applied to various industries.




Cl-P181


18


74.8


7.2


<0.2





645


670


8.6


Lowest melting range & best fluidity among the copper-phosphorus series.




Cl-P201


20


74


6


<0.2





630


660


8.7


Better for large quantity of brazing than others.




Cl-Sn7


-


86.25


6.75


Sn 7





650


700


8.0


Can be used to instead of CI-002 or CI-005. Good fluidity.